100/140/250 多模光纖（100/140/250μm multimode fiber）
in
This specification conforms to the requirement of IEC 60793 A1d.
|
OPTICAL CHARACTERISTICS
|
|||
|
Characteristics
|
Conditions
|
Specified Values
|
Unit
|
|
Attenuation Coefficient
|
850 nm
|
≦ 4.0
|
〔dB/km〕
|
|
|
1300 nm
|
≦ 1.5
|
〔dB/km〕
|
|
Numerical Aperture
|
|
0.290 ± 0.015
|
|
|
Bandwidth
|
850 nm
|
≧ 150
|
〔MHz·km〕
|
|
(*Higher bandwidth available upon request)
|
1300 nm
|
≧ 200
|
〔MHz·km〕
|
|
BACKSCATTER CHARACTERISTICS
|
|||
|
Attenuation Directional Uniformity
|
≦ 0.05
|
〔dB/km〕
|
|
|
Attenuation Uniformity
|
|
≦ 0.05
|
〔dB〕
|
|
Group Index of Refraction
|
850 nm
|
1.492
|
|
|
|
1300 nm
|
1.487
|
|
|
PHYSICAL CHARACTERISTICS
|
|||
| Core Diameter | 100 ± 4.0 | 〔µm〕 | |
| Core Non- circularity | ≦ 5 | 〔%〕 | |
|
Core / Cladding Concentricity Error
|
≦ 3.0
|
〔µm〕
|
|
|
Cladding Diameter
|
|
140 ± 3
|
〔µm〕
|
|
Cladding Non-Circularity
|
|
≦ 2.0
|
〔%〕
|
|
Coating Diameter
|
245 ± 10
|
〔µm〕
|
|
|
Clad/Coat Concentricity Error
|
|
≦ 10
|
〔µm〕
|
|
Fiber curl
|
|
≧ 2
|
〔m〕
|
|
Proof Test
|
|
100
|
〔kpsi〕
|
|
Bend Induced Attenuation at 1300 nm
|
≦ 0.5
|
〔dB〕
|
|
|
(100 turns around a mandrel of 75 mm diameter)
|
|
|
|
|
Average Coating Strip Force
|
≧ 1.3
|
〔N〕
|
|
|
Length (Typical)
|
|
1.1～8.8
|
〔km〕
|
|
ENVIRONMENTAL CHARACTERISTICS
|
|||
|
Temperature Dependence at 850 nm and 1300 nm
|
≦ 0.2
|
〔dB/km〕
|
|
|
Induced Attenuation – 60°C to +85°C
|
|
|
|
|
Watersoak Dependence at 850 nm and 1300 nm
|
≦ 0.2
|
〔dB/km〕
|
|
|
Induced Attenuation at 20°C for 30 days
|
|
|
|
|
Damp Heat Dependence at 850 nm and 1300 nm
|
≦ 0.2
|
〔dB/km〕
|
|
|
Induced Attenuation at 85°C, 85%R.H., 30 days
|
|
|
|
| Dynamic Tension Strength |
≧ 550
|
〔kpsi〕
|
|
| Median Tensile Strength of Unaged Fiber (0.5 m) | |||
| Dynamic Fatigue Constant (nd) | 20 | ||